Juno Siliconized High Temperature Enamel
Enamel resistant to 200-250 ° C. Formulated based on silicone resin and pigmented alkyd according to color. Cleaning and dissolving with QUICK DRYING Solvent (D-17).
- 15/4 L.
- RAL colors (05.899)
Preparation
IRON AND NEW STEEL. Abrasive blasting up to Sa 2 ½ grade according to ISO 8501-1, leaving a roughness profile between 20-50 µ. Peeling paint coatings, mill scale, rust and foreign matter will be removed. Any remaining trace of contamination should only show up as small circular spots or stripes. Then prime with a primer resistant to the desired temperature. STEEL-IRON PRIMED. Peeling paint coatings will be removed using wire brushes, scrapers, pre-made synthetics containing abrasives, and rust chipping hammers. Subsequently, manual degreasing of the surface eliminating salts and other contaminants with high pressure fresh water. Recommended prior shot blasting Sa 2½. Subsequently a suitable primer will be applied.
Use
INSIDE-OUTSIDE
Heat resistant enamels are indicated for the protection of primed metal surfaces, subjected to temperatures of up to 200ºC in moderately aggressive marine or industrial environments.
Application
Brush, roller, spray gun, airless spray. After application, forced drying must be carried out at temperatures of 200ºC for 30 minutes. In practice, in the painting of fixed and bulky installations, the curing of the paint can be carried out with their own operation. It must also be taken into account that the painted parts cannot be subjected to sudden increases in temperature, in this case blisters would form, but 200ºC must be reached slowly.